Authentic American Style SPC Flooring
Description:
Item：YS1089-1-EIR
Thickness: 4.0mm~8.0mm
Wear Layer: 0.2mm~0.7mm
Underlay（Optional）：EVA/ IXPE, 1.0mm~2.0mm
Size：7.25’’ X 48’’/ 6’’X48’’/ 9’’X48’’/ 7’’X36’’/ 6’’X36’’/ 9’’X36’’/ Customization
SPC Vinyl flooring vividly mimics the color and grains of wood flooring while it isn’t real wood. Even a professional could be fooled by his eyes without touching it. It combines the beauty of natural wood with modern technology. With a much more cost-effective price compared with solid wood floor, it is uniquely perfect for commercial and domestic use.
Similar to dry back vinyl plank, SPC flooring is comprised of multiple layers that are fused together. However, unlike dry back flooring, SPC flooring feature a rigid core and is harder.
The high dense rigid core offers better resistance from scratches, or dents from heavy items or furniture being placed on top of it and makes the flooring less susceptible to expansion in cases of extreme temperature change. Topical spills or moisture is not an issue if properly cleaned in time. SPC was originally created for commercial markets because of their durability. However, homeowners have started using rigid core as well because of its ease of installation, design options and durability. It is important to note that some SPC varies from commercial to light commercial use depending on its core thickness and wear layer thickness.
Though installing over a flat surface is always a good practice to be in, floor imperfections are more easily hidden with SPC flooring due to its rigid core composition.
|
Specification |
|
|
Surface Texture |
Wood Texture |
|
Overall Thickness |
4mm |
|
Underlay（Optional） |
IXPE/EVA(1mm/1.5mm) |
|
Wear Layer |
0.2mm. (8 Mil.) |
|
Width |
7.25” (184mm.) |
|
Length |
48” (1220mm.) |
|
Finish |
UV Coating |
|
Locking System |
|
|
Application |
Commercial & Residential |
Technical Data：
| SPC RIGID-CORE PLANK TECHNICAL DATA | ||
|
Technical Information |
Test Method |
Results |
|
Dimensional |
EN427 & |
Pass |
|
Thickness in total |
EN428 & |
Pass |
|
Thickness of wear layers |
EN429 & |
Pass |
|
Dimensional Stability |
IOS 23999:2018 & ASTM F2199-18 |
Manufacturing Direction ≤0.02% (82oC @ 6hrs) |
|
Across Manufacture Direction ≤0.03% (82oC @ 6hrs) |
||
|
Curling (mm) |
IOS 23999:2018 & ASTM F2199-18 |
Value 0.16mm(82oC @ 6hrs) |
|
Peel Strength (N/25mm) |
ASTM D903-98(2017) |
Manufacturing Direction 62 (Average) |
|
Across Manufacture Direction 63 (Average) |
||
|
Static Load |
ASTM F970-17 |
Residual Indentation:0.01mm |
|
Residual Indentation |
ASTM F1914-17 |
Pass |
|
Scratch Resistance |
ISO 1518-1:2011 |
No penetrated the coating at the load of 20N |
|
Locking Strength(kN/m) |
ISO 24334:2014 |
Manufacturing Direction 4.9 kN/m |
|
Across Manufacture Direction 3.1 kN/m |
||
|
Colour Fastness to Light |
ISO 4892-3:2016 Cycle 1 & ISO105–A05:1993/Cor.2:2005& ASTM D2244-16 |
≥ 6 |
|
Reaction to fire |
BS EN14041:2018 Clause 4.1 & EN 13501-1:2018 |
Bfl-S1 |
|
ASTM E648-17a |
Class 1 |
|
|
ASTM E 84-18b |
Class A |
|
|
VOC Emissions |
BS EN 14041:2018 |
ND - Pass |
|
ROHS/Heavy Metal |
EN 71-3:2013+A3:2018 |
ND - Pass |
|
Reach |
No 1907/2006 REACH |
ND - Pass |
|
Formaldehyde emission |
BS EN14041:2018 |
Class: E 1 |
|
Phthalate Test |
BS EN 14041:2018 |
ND - Pass |
|
PCP |
BS EN 14041:2018 |
ND - Pass |
|
Migration of Certain Elements |
EN 71 – 3:2013 |
ND - Pass |
Packing Infornation：
|
Packing Information(4.0mm) |
|
|
Pcs/ctn |
12 |
|
Weight(KG)/ctn |
22 |
|
Ctns/pallet |
60 |
|
Plt/20’FCL |
18 |
|
Sqm/20’FCL |
3000 |
|
Weight(KG)/G.W |
24500 |